The effect of nanoparticles TiO2 on the flexural strength of acrylic resin denture plate

Edwin Tandra, Endang Wahyuningtyas, Erwan Sugiatno


Introduction: Acrylic resin is still the most commonly used denture base material due to its ideal properties. However, acrylic resin denture fractures are still considered a major unsolved problem thus the addition of nanoparticles as filler was performed to increase its mechanical properties. The purpose of this study was to discovered the effect of nanoparticles TiO2 on the flexural strength of acrylic resin denture plate. Method: This study used 27 heat-cured acrylic resin specimens sized 65 x 10 x 2.5 mm. The samples were divided into three concentration groups (n = 9), the control group; 1% of nanoparticles TiO2; and 3% of nanoparticles TiO2. The flexural strength was tested using the Universal Testing Machine. All data were analysed using the one-way ANOVA test with 95% confidence level then continued with the Least Significant Difference (LSD) test. Results: There were significant flexural strength differences in different concentration of nanoparticles TiO2. The highest flexural strength value was found in the 1% of nanoparticles TiOgroup (106.99 ± 6.09 MPa), whilst the lowest flexural strength value was found in the 3% of nanoparticles TiOgroup (91.64 ± 5.38 MPa). Significant flexural strength difference was found between the control group and the 1% of nanoparticles TiOgroup, and also between the 1% of nanoparticles TiOgroup with the 3% of nanoparticles TiOgroup (p < 0.05). Conclusion: From this study can be concluded that concentration of 1% of nanoparticles TiO2 was able to increase the flexural strength of acrylic resin denture plate.


Titanium dioxide, flexural strength, acrylic resin

Full Text:



Gunadi HA, Margo A, Burhan LK, Suryatenggara F, Setiabudi I. Textbook of removable partial prosthodontics. 2nd ed. Jakarta: Hipokrates; 1995. p. 379-90.

Sakaguchi RL, Powers JM. Craig’s Restorative Dental Materials. 13th ed. St. Louis: Mosby-Elsevier; 2013. p. 51-91, 149-57.

McCabe JF, Walls AWG. Applied Dental Materials. 9th ed. Hoboken: Wiley-Blackwell; 2008. p. 3-5, 101-23.

Yoshida K, Takahashi Y, Hamanaka I, Kawaguchi T, Sasaki H, Shimizu H. Reinforcing Effect of Glass Fiber-Reinforced Composite Reinforcement on Flexural Strength at Proportional Limit of a Repaired Denture Base Resin. Acta Biomater Odontol Scand. 2015 Oct 12;1(2-4):81-85. DOI: 10.3109/23337931.2015.1099441

Da Silva LH, Feitosa SA, Valera MC, De Araujo MA, Tango RN. Effect of the Addition of Silanated Silica on The Mechanical Properties of Microwave Heat-Cured Acrylic Resin. Gerodontology. 2012 Jun;29(2):e1019-23. DOI: 10.1111/j.1741-2358.2011.00604.x

Alnamel HA, Mudhaffer M. The effect of Silicon Dioxide Nano-Fillers Reinforcement on Some Properties of Heat Cured Polymethyl Methacrylate Denture Base Material. J Bagh Coll Dent. 2014 Mar;26(1):32-6.

Sodagar A, Bahador A, Khalil S, Shahroudi AS, Kassaee MZ. The Effect of TiO2 and SiO2 Nanoparticles on Flexural Strength of Poly (Methyl Methacrylate) Acrylic Resins. J Prosthodont Res. 2013 Jan;57(1):15-9. DOI: 10.1016/j.jpor.2012.05.001

Shirkavand S, Moslehifard E. Effect of TiO2 Nanoparticles on Tensile Strength of Dental Acrylic Resins. J Dent Res Dent Clin Dent Prospects. 2014 Autumn; 8(4): 197–203. DOI: 10.5681/joddd.2014.036

Alwan SA, Alameer SS. The Effect of The Addition of Silanized Nano Titania Fillers on Some Physical and Mechanical Properties of Heat Cured Acrylic Denture Base Materials. J Bagh Coll Dent. 2015 Mar;27(1):86-91.

Sideridou ID, Karabela MM. Effect of The Amount of 3-Methacyloxypropyltrimethoxysilane Coupling Agent on Physical Properties of Dental Resin Nanocomposites. Dent Mater. 2009 Nov;25(11):1315–24. DOI: 10.1016/

Powers JM. Craig's Restorative Dental Materials. 12th ed. St. Louis: Mosby-Elsevier; 2006. p. 514-24.

Harini P, Mohamed K, Padmanabhan TV. Effect of Titanium Dioxide Nanoparticles on The Flexural Strength of Polymethylmethacrylate: An In Vitro Study. Indian J Dent Res. 2014 Jul-Aug;25(4):459-63. DOI: 10.4103/0970-9290.142531

Ghahremani L, Shirkavand S, Akbari F, Sabzikari N. Tensile Strength and Impact Strength of Color Modified Acrylic Resin Reinforced with Titanium Dioxide Nanoparticles. J Clin Exp Dent. 2017 May; 9(5): e661–e665. DOI: 10.4317/jced.53620

Ahmed MA, El-Shennawy M, Althomali YM, Omar AA. Effect of Titanium Dioxide Nano Particles Incorporation on Mechanical and Physical Properties on Two Different Types of Acrylic Resin Denture Base. World J Nano Sci Engineer. 2016 Sep;6(3):111-9. DOI: 10.4236/wjnse.2016.63011

Nazirkar G, Bhanushali S, Singh S, Pattanaik B, Raj N. Effect of Anatase Titanium Dioxide Nanoparticles on The Flexural Strength of Heat Cured Poly Methyl Methacrylate Resins: An In-Vitro Study. J Indian Prosthodont Soc. 2014 Dec;14(Suppl 1):144-9. DOI: 10.1007/s13191-014-0385-8

Salman TA, Khalaf HA. The Influence of Adding of Modified ZrO2-TiO2 Nanoparticles on Certain Physical and Mechanical Properties of Heat Polymerized Acrylic Resin. J Bagh Coll Dent. 2015 Sep;27(3):33-9.

Acosta-Torres LS, López-Marín LM, Núñez-Anita RE, Hernández-Padrón G, Castaño VM. Biocompatible of Metal-Oxide Nanoparticles Nanotechnology Improvement of Conventional Prosthetic Acrylic Resins. J Nanomater. 2011;2011:1-8. DOI: 10.1155/2011/941561


Article metrics

Abstract views : 0 | views : 0


  • There are currently no refbacks.

Copyright (c) 2018 Padjadjaran Journal of Dentistry

Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.

 Visitor Stat

Creative Commons License
Padjadjaran Journal of Dentistry is licensed under a Creative Commons Attribution 4.0 International License